LiTaO3 crystal is also widely used E-O crystal, due to its optical, NLO and E-O poperties similar to those of LiNbO3 crystal, but with higher damage threshold (> 500 MW/cm2 for ns pulsed). Main properties include:

• Transparent Range: 0.4 - 5.0 μm; E-O Coefficient: r33=30.4; 

• Refractive Indices: no=2.176, ne=2.180 @ 633 nm.

Maximum LiTaO3 SAW wafer size we can offer is 6 inch in diameter.

Red Optronics provide LiTaO3 in as-cut boules, wafers or slices. Our production capabilities include:

Boules: 

• Diameter: f40mm ~ 102mm 

• Length: 50mm ~ 150mm 

• Orientation: X, Z, 36�Y, 42�Y, 128�Y 

• Polish: 0.016mm 

Wafers: 

• Diameter: f40mm ~ 102mm 

• Length: 0.2~1.2mm 

• Orientation: X, Z, 36�Y, 42�Y, 128�Ys 

• Flatness: 
  <10mm for f40 ~ 65mm
  <15mm for f65 ~ 102mm 

• Bow: 
  <20mm for f40~ 65 mm, 
  <40mm for f65 ~102mm 

Slices: 
Size: 100x45x1.5mm ~ 120x40x2mm 

Notes:
To inquire or order LiTaO3 crystals, please provide specifications as detailed in above.
 

Physical and Optical Properties   Crystal Structure:  Trigonal, space group R3c,Point group 3m  Cell Parameters:  a=5.154A,c=13.781A Melting point: 1650�C Curie Temperature:  607�C  Mohs hardness:  5.5  Density:  7.46 g/cm3  Dielectric Constant:  ξ11/ξ0 51.7 ξ33/ξ0 44.5  Elastic Stiffness Coefficient:  CE11 2.33(X 1011 N/m2) CE33 2.77(X 1011 N/m2)  Piezoelectric Strain Constant:  d22 2.4(X 10-11 C/N) d33 0.8(X 10-11 C/N)  Transmission range:  400-4500nm  Electro-optical coefficients:  r33 30.4pm/V  Refractive index at 632.8nm: no=2.176, ne=2.180 Aperture